Test method for coating amount of PTP aluminum foil protective agent

Test method for coating amount of PTP aluminum foil protective agent

2022-12-12

Test method for coating amount of PTP aluminum foil protective agent

The protective agent layer of PTP aluminum foil is a dense cross-linked resin layer formed by high temperature curing. It is difficult to completely wipe the coating in a short time by the solvent wiping method commonly used now, and it is difficult to obtain accurate coating quantity value. Moreover, the repeatability of sample test results is also very poor. Therefore, a more effective test method for the coating quantity of PTP aluminum foil protective layer is found, It is of great practical value to guide the production of such products.

According to the material characteristics of PTP aluminum foil and the comparison of the advantages and disadvantages of various detection methods, we finally believe that the "burning method" is the most suitable for the rapid detection of the amount of protective agent coating:

In this method, the PTP aluminum foil sample is placed in a muffle furnace, maintained at a certain temperature for a certain time, and the PTP aluminum foil coated with the protective agent layer is baked at high temperature, so that the protective agent layer is completely oxidized and gasified. The coating amount of the protective agent layer can be calculated by detecting the quality of the aluminum foil before and after the high-temperature baking.

1、 Instruments and reagents:

10cm * 10cm standard cutting plate, blade, analytical balance (precision: 1/10000 g), muffle furnace, glass plate, stainless steel tweezers, ethyl acetate (analytical pure), absorbent cotton

2、 Test method:

1. Select the aluminum foil sample sheet for drug packaging with flat surface and no wrinkles, cut 5 test samples with a blade and a 10cm * 10cm standard cutting plate, and control the deviation of the width and length of the sample within ± 0.5mm

2. Weigh the cut sample (W1) on the balance.

3. Put the printing face of the aluminum foil on a glass plate, and use stainless steel tweezers to clamp the degreased cotton dipped in ethyl acetate to wipe the heat-sealing coating surface of the aluminum foil until no obvious marks can be identified when the surface is observed with naked eyes. (Note: The cotton ball dipped with ethyl acetate shall not have the liquid of ethyl acetate dripping. The circular wiping method from the center to the edge shall be used for wiping. The edge of the aluminum foil must be laid flat on the glass plate, and the linear wiping method shall be used for wiping. The other side of the aluminum foil shall not be affected during the whole process as much as possible). If the cotton ball has been wiped with the printing coating, replace it with a new cotton ball.

4. After wiping the heat-sealing coating, put the aluminum foil in a ventilated place and place it at room temperature for 2 minutes.

5. Then weigh the weight (W2) on the analytical balance

6. Place the above aluminum foil on the sample shelf in the muffle furnace preheated to 550-600 ℃. After waiting for a period of time, take out the coated aluminum foil and place it at room temperature. (The black ink may not completely volatilize the pigment, and its impact can be temporarily ignored for the products with general printed text patterns. If the printed patterns are large, the weight impact of the ink binder and the pigment should be considered)

7. Then weigh the weight (W3) on the analytical balance

Note: If the test sample has no adhesive layer, omit the operations in 2, 3 and 4.

8. Result calculation:

(W1-W2) × 100=weight of heat seal layer (g/m2)

(W2-W3) × 100=weight of printing layer/protective layer (g/m2) (when the sample has adhesive layer)

(W1-W3) × 100=weight of printing layer/protective layer (g/m2) (when the sample has no adhesive layer)

W3 × 100=weight of aluminum foil layer (g/m2)

Calculate and report the test results and average values of all individual samples to the nearest 0.01g/m2.


主站蜘蛛池模板: 亚洲AV无码乱码在线观看浪潮 | 亚洲欧洲精品成人久久曰影片 | 日韩精品熟女一区二区三区中文 | 诱人的女邻居9中文观看 | 深夜草逼逼 | 国内精品免费久久影院 | 中国jjzz| avv天堂| 国产69精品久久久熟女 | 粗好大用力好深快点漫画 | 久久是热频国产在线 | 男女床上黄色 | 久久日韩精品无码一区 | 中文中幕无码亚洲视频 | 三级在线观看网站 | 日韩欧美一区二区三区在线视频 | 亚洲精品国偷拍自产在线 | 97在线观看免费视频 | 欧美高清视频www夜色资源网 | 俄罗斯呦呦 | 最新精品学生国产自在现拍 | 久青草国产观看在线视频 | 久久影院中文字幕 | 一级毛片免费下载 | 伊人久久久久久久久久 | 99国产电影 | 亚洲精品乱码久久久久久中文字幕 | 日本日本熟妇中文在线视频 | 免费看大黄高清网站视频在线 | 黑人强伦姧人妻日韩那庞大的 | 久久国产乱子伦精品免费M 久久国产露脸老熟女熟69 | 国产在线高清亚洲精品一区 | 亚洲国产精品一区二区三区在线观看 | 日本中文字幕巨大的乳专区 | 永久免费在线看mv | 帅哥男男GV在线1080P | 69久久国产精品热88人妻 | 芭乐视频网页版在线观看 | 99久久免费国产精精品 | 国模丽丽啪啪一区二区 | 青柠在线观看视频在线高清 |